Backcountry Forum

Make Your Own Gear
Backpacking Forums
backcountry gear

---- Our Gear Store ----
The Lightweight Gear Store

Bivy Bags
Sleeping Bags
Sleeping Pads
Snow Sports
Winter Kitchen


Avalanche Gear
Hats, Gloves, & Gaiters


Ultralight Backpacks
Ultralight Bivy Sacks
Ultralight Shelters
Ultralight Tarps
Ultralight Tents
Ultralight Raingear
Ultralight Stoves & Cookware
Ultralight Down Sleeping Bags
Ultralight Synthetic Sleep Bags
Ultralight Apparel

the Titanium Page
WM Extremelite Sleeping Bags


Sleeping Bags


Ropes & Cordage
Protection & Hardware
Carabiners & Quickdraws
Climbing Packs & Bags
Big Wall
Rescue & Industrial






Men's Footwear
Women's Footwear


Mens Apparel
Womens Apparel


Black Diamond
Granite Gear
La Sportiva


Top Brands
All Brands

 Backpacking Equipment 

Sleeping Bags
Water Treatment

 Backcountry Gear Clearance

Stay Healthy--Eat Well


Mary Janes Farm Organic Backcountry Meals


Natural High


Page 2 of 2 < 1 2
Topic Options
Rate This Topic
#123037 - 10/28/09 08:12 PM Re: Knife making [Re: Pika]
Kent W Offline

Registered: 10/15/09
Posts: 607
Loc: IL.
Pika what is the mehod to heat treat a saw blade? I have treated mild steel shafts bye heating to a straw color and burying in a can of powdered lime. This greatly slows the cooling process. Havent broke one yet but havent stressed one to terrible either. As for treating a file to make less brittle would simple annealing help?
To all those reading, I sugested a file for knife making because most people have a old small file around. This makes it a inexpensive way to start. Hard and Brittle, yes as Pika says . Good practice in begining knife making? I think so, with care they can be servicable, Best maybe not ,but servicable.

#123043 - 10/28/09 09:32 PM Re: Knife making [Re: Kent W]
Pika Online   content

Registered: 12/08/05
Posts: 1746
Loc: Rural Southeast Arizona
Heat treating is both a science and an art. The first step is to harden the steel. To harden, one takes the annealed, formed piece and heats it to what is termed the critical point. This is often described as a "cherry red heat" but it differs for various steel compositions. The best way to determine the critical point is to heat the steel until a magnet is no longer attracted to the hot steel. Then, you quickly quench the piece (here we are talking about knife blades) in a liquid.

The best liquid to use for quenching is often a matter of dispute. At one time, sperm whale-oil was highly regarded. I use SAE 30 motor oil. Others use a stiff brine. Basically, the quicker the steel is cooled, the harder it is. Brine is used for files, it produces a super hard steel. Using oil will slow the cooling somewhat and will produce a quenched steel that has a bit of toughness. When quenching, it is important to plunge the knife quickly and straight into the quenching liquid. Hesitation or lack of a straight stab can cause the blade to warp.

Once you have quenched (and hardened) the blade, you are ready to heat treat. There are two ways to do this. One is to carefully heat the hardened blade to the temperature stated on the specification sheet to produce a give Rockwell Hardness. This requires an oven and accurate temperature control. The entire blade will be the same hardness and toughness using this procedure. Most commercial knives are done using this process and it works pretty well.

The method I use is called differential hardening or differential tempering and is done by "running the colors". You don't need an oven or thermometer; I have a coal forge and use that. You first polish the blade to a good shine. Then, you heat a bar of iron in a forge (or charcoal fire) to a red heat. You then place the back of the polished blade on the hot iron and watch the colors develop. What you are looking for is for the first straw color to just reach the cutting edge along the full length of the blade. This takes a bit of practice because you have to move the knife blade around to push the straw color ahead in places and hold it back in others. You do not heat and let the straw color reach the edge and then quench again, you let the colors move slowly across the blade and stop by themselves. Ideally, when you are finished, the bulk of the blade will be blue, about 1/8" of the edge will be straw and the other colors will be compressed between the blue and straw. When done this way, most of the blade is springy; springs are tempered to blue. But, the edge with its straw color is just a bit softened from the hardened state with a bit of toughness. Steel with 1% carbon heated to a faint straw will hold a fine edge for a long time.

I probably used up a dozen forged knife blades before I got adequately good at differential hardening. I still screw up on about one out of five blades. That is one reason I like carbon steel like 1095 or good saw steel. Unless you get it hot enough to burn the carbon out you can re-harden and try again. I would sure hate to have to do a sword this way though.
May I walk in beauty.

#123130 - 10/29/09 09:27 PM Re: Knife making [Re: Pika]
Kent W Offline

Registered: 10/15/09
Posts: 607
Loc: IL.
Thank You. I am going to try a small knife this winter. That brings back a bit of memory. I have several old carbon saw blades. Even a couple of 28 inch sawmill blades. Im going to try your method! I Cut and Pasted your instructions and printed them as well.

#124283 - 11/23/09 09:51 PM Re: Knife making [Re: Bear Cavalry]
Ecrow Offline

Registered: 02/02/08
Posts: 85
Loc: N. New Mexico
Pika is right about steel stock. So here is the compromise: buy a sawzall blade that you like, carefully heat it until it loses its magnetism (cherry) and let it cool off slowly. (insulated). Then work it into your shape but don't fully sharpen the cutting surface or it will burn and chip. Heat it until it looses its magnetism and quench it in automatic transmission fluid diluted with a little solvent. Be careful because the smoke can flash fire, use long tongs and gloves. Then put the rough blank in the oven @ 350-400 for an hour. You can always experiment with scrap to find a hard AND flexible heat treatment. Forging with a torch isn't too hard either. The tool most used is a belt sander. It's easy and fun, pretty soon you get to reading a lot and buying flat stock on ebay.
Live to tell.

Page 2 of 2 < 1 2

Shout Box

Highest Quality Lightweight Down Sleeping Bags
Western Mountaineering Sleeping Bags
Lite Gear Talk - Featured Topics
Looking for a lite, compact and cheap'ish day pack
by willie1280
08:54 AM
Trying To (you guessed it) Reduce Weight
by Bill Kennedy
03:15 AM
Are small cheap solar chargers any good?
by Wasatch
03/19/18 01:38 PM
Backcountry Discussion - Featured Topics
Check out my FIRST hiking video
by TheHkngGrdnr
04:33 AM
I chose Sawtooth over Medicine bow
by toddfw2003
03/14/18 11:11 PM
Anyone use Vasque Breeze 3 non gortex?
by toddfw2003
03/14/18 10:44 PM
Make Your Own Gear - Featured Topics
Whitney Jacket Cuffs
by Bill Kennedy
03/07/18 05:01 AM
Joann fabrics and quilt supplies
by sashurlow
05/02/15 07:32 AM
Featured Photos
Breakneck Ridge, New York
May 2012 Eclipse, Lassen Park
New Years Eve 2011
Trip Report with Photos
Seven Devils, Idaho
Oat Hill Mine Trail 2012
Dark Canyon - Utah
Who's Online
0 registered (), 30 Guests and 0 Spiders online.
Key: Admin, Global Mod, Mod
Newest Members
TheHkngGrdnr, banjolady, Soughted, Yanksguy, momu119
12536 Registered Users
Forum Links
Site Links
Family Hiking
Lightweight Gear Store
Backpacking Book Store
Lightweight Zone
Hiking Essentials

Outdoor Gear Daily Deals
Outlets, Sales, Bargains

Our long-time Sponsor, - The leading source for ultralite/lightweight outdoor gear:

Backcountry Forum

Since 1996 - the Original Backcountry Forum
Copyright © The Lightweight Backpacker &